Description

Schott D263M is a colorless borosilicate glass with a very low iron content. It meets requirements laid down in ISO 8255-1. It has high spectral transmission, excellent flatness and a refractive index finely adapted to microscopes. Very good resistance to chemical attack. Fire polished.


Applications

The characteristics of this special composition substrate glass makes it suitable for a variety of applications, including:

  • Microscope cover glass
  • Thin film substrate
  • Touch control panels
  • Solar cells
  • Sensors


Mechanical Properties

Density p in g/cm3

2.51

Stress optical coefficient C in 1.02 · 10-12 m2/N

3.4

Young's Modulus E in kN/mm2

72.9

Poisson number µ

0.208

Modulus of torsional shear G in kN/mm2

30.1

Knoop hardness HK100

590


Electrical Properties

Dielectric constant Ԑr at 1 MHz

6.7

Dielectrical loss factor tan δ at 1 MHz

61·10-4

Electrical volume resistance pD in Ω · cm at defined temperatures pD for alternating current 50 Hz

 

θ = 250°C

1.6 · 108

 

θ = 350°C

3.5 · 106


Thermal Characteristics

Viscosity and Temperature

Description

Viscosity log Ƞ [dPas]

Temperature θ [°C]

Strain point

14.5

529

Annealing point

13.0

557

Softening point

7.6

736

Transformation temperature in °C

557



Expansion factor α

Coefficient of thermal expansion α (20-300°C) in 10-6 K-1
(static measurement)

7.2


Spectral Transmittance (d=0.15mm)

spectral transmittance


Optical Properties of Schott D263M

Refractive indicies
ne (λ = 546.1nm): 1.5255 ±0.0015
nD (λ = 589.3nm): 1.5230
Above value ve: 55

The light transmittance for a thickness of 0.15 mm is TVD65 in % (d=0.15mm) = 91.7 ± 0.3%. In the visible range of the spectrum D26 M is without absorption. The excellent UV absorption properties make D263M an ideal material for use in fluorescence microscopy.


Thickness* Dimension of Schott D263M

No. 0 = (0.08 - 0.12mm)
No. 1 = (0.13 -0.16mm)
No. 1.5 = (0.16 - 0.19mm)
 No. 2 = (0.19 - 0.23mm)

*Not all thicknesses available in all sizes


Chemical Properties of Schott D263M

Hydrolytic resistance: (DIN ISO 719)
Hydrolytic class: HGB 1
Equivalient of alkali (Na2O) per gram of glass grains in µg/g: 20
Acid resistance (DIN 12 116)
Acid class: S 2
Half surface weight loss after 6 hours mg/dm2: 1.4
Alkali resistance: (DIN ISO 695)
Class: A 2
Surface weight loss after 3 hours mg/dm2: 88



Chemical Composition of Schott D263M

SiO2 = 64.1%
B2O3 = 8.4%
Al2O3= 4.2%
Na2O = 6.4%
K2O = 6.9%
MgO -
CaO -
BaO -
ZnO = 5.9%
TiO2 = 4.0%
As2O3 -
Sb2O3 = 0.1%


Was this article helpful?

That’s Great!

Thank you for your feedback

Sorry! We couldn't be helpful

Thank you for your feedback

Let us know how can we improve this article!

Select at least one of the reasons

Feedback sent

We appreciate your effort and will try to fix the article